EN 1.4981 Stainless Steel vs. EN 1.6553 Steel

Both EN 1.4981 stainless steel and EN 1.6553 steel are iron alloys. They have 66% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4981 stainless steel and the bottom bar is EN 1.6553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
210 to 240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
19 to 21
Fatigue Strength, MPa 210
330 to 460
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 610
710 to 800
Tensile Strength: Yield (Proof), MPa 240
470 to 670

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.7
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.6
Embodied Energy, MJ/kg 67
21
Embodied Water, L/kg 150
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
130 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 150
600 to 1190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
25 to 28
Strength to Weight: Bending, points 20
23 to 24
Thermal Diffusivity, mm2/s 4.3
10
Thermal Shock Resistance, points 14
21 to 23

Alloy Composition

Carbon (C), % 0.040 to 0.1
0.23 to 0.28
Chromium (Cr), % 15.5 to 17.5
0.4 to 0.8
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 59.6 to 66.7
95.6 to 98.2
Manganese (Mn), % 0 to 1.5
0.6 to 1.0
Molybdenum (Mo), % 1.6 to 2.0
0.15 to 0.3
Nickel (Ni), % 15.5 to 17.5
0.4 to 0.8
Niobium (Nb), % 0.4 to 1.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.3 to 0.6
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0
0 to 0.030