EN 1.4981 Stainless Steel vs. EN AC-44500 Aluminum

EN 1.4981 stainless steel belongs to the iron alloys classification, while EN AC-44500 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4981 stainless steel and the bottom bar is EN AC-44500 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
68
Elastic (Young's, Tensile) Modulus, GPa 200
72
Elongation at Break, % 39
1.1
Fatigue Strength, MPa 210
110
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
27
Tensile Strength: Ultimate (UTS), MPa 610
270
Tensile Strength: Yield (Proof), MPa 240
160

Thermal Properties

Latent Heat of Fusion, J/g 290
570
Maximum Temperature: Mechanical, °C 940
170
Melting Completion (Liquidus), °C 1440
590
Melting Onset (Solidus), °C 1400
580
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 16
130
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
33
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
120

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.5
Density, g/cm3 7.9
2.5
Embodied Carbon, kg CO2/kg material 4.8
7.7
Embodied Energy, MJ/kg 67
140
Embodied Water, L/kg 150
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
2.6
Resilience: Unit (Modulus of Resilience), kJ/m3 150
180
Stiffness to Weight: Axial, points 14
16
Stiffness to Weight: Bending, points 24
55
Strength to Weight: Axial, points 21
29
Strength to Weight: Bending, points 20
36
Thermal Diffusivity, mm2/s 4.3
57
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 0
83.7 to 89.5
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 15.5 to 17.5
0
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 59.6 to 66.7
0 to 1.0
Magnesium (Mg), % 0
0 to 0.4
Manganese (Mn), % 0 to 1.5
0 to 0.55
Molybdenum (Mo), % 1.6 to 2.0
0
Nickel (Ni), % 15.5 to 17.5
0
Niobium (Nb), % 0.4 to 1.2
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0.3 to 0.6
10.5 to 13.5
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.25