EN 1.4983 Stainless Steel vs. EN 1.4841 Stainless Steel

Both EN 1.4983 stainless steel and EN 1.4841 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 83% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4983 stainless steel and the bottom bar is EN 1.4841 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
32
Fatigue Strength, MPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Shear Strength, MPa 430
430
Tensile Strength: Ultimate (UTS), MPa 630
650
Tensile Strength: Yield (Proof), MPa 230
260

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Maximum Temperature: Corrosion, °C 520
440
Maximum Temperature: Mechanical, °C 940
1150
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
25
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.1
4.3
Embodied Energy, MJ/kg 56
62
Embodied Water, L/kg 150
190

Common Calculations

PREN (Pitting Resistance) 24
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
170
Resilience: Unit (Modulus of Resilience), kJ/m3 140
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 14
15

Alloy Composition

Boron (B), % 0.0015 to 0.0060
0
Carbon (C), % 0.040 to 0.080
0 to 0.2
Chromium (Cr), % 16 to 18
24 to 26
Iron (Fe), % 61.8 to 69.6
47.1 to 55.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 12 to 14
19 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.75
1.5 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0.4 to 0.8
0