EN 1.4986 Stainless Steel vs. ACI-ASTM CB7Cu-1 Steel

Both EN 1.4986 stainless steel and ACI-ASTM CB7Cu-1 steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4986 stainless steel and the bottom bar is ACI-ASTM CB7Cu-1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
300 to 420
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
5.7 to 11
Fatigue Strength, MPa 350
420 to 590
Impact Strength: V-Notched Charpy, J 57
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 750
960 to 1350
Tensile Strength: Yield (Proof), MPa 560
760 to 1180

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1500
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
13
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.8
2.6
Embodied Energy, MJ/kg 67
38
Embodied Water, L/kg 150
130

Common Calculations

PREN (Pitting Resistance) 22
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
71 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 790
1500 to 3590
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26
34 to 48
Strength to Weight: Bending, points 23
28 to 35
Thermal Diffusivity, mm2/s 4.0
4.6
Thermal Shock Resistance, points 16
32 to 45

Alloy Composition

Boron (B), % 0.050 to 0.1
0
Carbon (C), % 0.040 to 0.1
0 to 0.070
Chromium (Cr), % 15.5 to 17.5
15.5 to 17.7
Copper (Cu), % 0
2.5 to 3.2
Iron (Fe), % 59.4 to 66.6
72.3 to 78.4
Manganese (Mn), % 0 to 1.5
0 to 0.7
Molybdenum (Mo), % 1.6 to 2.0
0
Nickel (Ni), % 15.5 to 17.5
3.6 to 4.6
Niobium (Nb), % 0.4 to 1.2
0 to 0.35
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0.3 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030