EN 1.4988 Stainless Steel vs. ASTM A299 Steel

Both EN 1.4988 stainless steel and ASTM A299 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4988 stainless steel and the bottom bar is ASTM A299 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
21 to 22
Fatigue Strength, MPa 230
230 to 250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 430
370 to 390
Tensile Strength: Ultimate (UTS), MPa 640
590 to 620
Tensile Strength: Yield (Proof), MPa 290
330 to 360

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 920
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 23
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 6.0
1.4
Embodied Energy, MJ/kg 89
19
Embodied Water, L/kg 150
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
290 to 350
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
21 to 22
Strength to Weight: Bending, points 21
20 to 21
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 14
17 to 18