EN 1.4988 Stainless Steel vs. SAE-AISI 8655 Steel

Both EN 1.4988 stainless steel and SAE-AISI 8655 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4988 stainless steel and the bottom bar is SAE-AISI 8655 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Fatigue Strength, MPa 230
290
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 430
390
Tensile Strength: Ultimate (UTS), MPa 640
620
Tensile Strength: Yield (Proof), MPa 290
410

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 920
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 23
2.6
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 6.0
1.5
Embodied Energy, MJ/kg 89
20
Embodied Water, L/kg 150
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
130
Resilience: Unit (Modulus of Resilience), kJ/m3 210
440
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 14
18

Alloy Composition

Carbon (C), % 0.040 to 0.1
0.51 to 0.59
Chromium (Cr), % 15.5 to 17.5
0.4 to 0.6
Iron (Fe), % 62.1 to 69.5
96.4 to 97.6
Manganese (Mn), % 0 to 1.5
0.75 to 1.0
Molybdenum (Mo), % 1.1 to 1.5
0.15 to 0.25
Nickel (Ni), % 12.5 to 14.5
0.4 to 0.7
Niobium (Nb), % 0.4 to 1.2
0
Nitrogen (N), % 0.060 to 0.14
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.3 to 0.6
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040
Vanadium (V), % 0.6 to 0.85
0