EN 1.5024 Steel vs. ASTM A372 Grade J Steel
Both EN 1.5024 steel and ASTM A372 grade J steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.5024 steel and the bottom bar is ASTM A372 grade J steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 470 | |
| 200 to 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1930 | |
| 650 to 1020 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 420 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 2.4 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 20 |
| Embodied Water, L/kg | 45 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 69 | |
| 23 to 36 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 21 to 29 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 20 to 58 | |
| 19 to 30 |
Alloy Composition
| Carbon (C), % | 0.42 to 0.5 | |
| 0.35 to 0.5 |
| Chromium (Cr), % | 0 | |
| 0.8 to 1.2 |
| Iron (Fe), % | 96.7 to 97.6 | |
| 96.7 to 97.8 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.75 to 1.1 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.015 |
| Silicon (Si), % | 1.5 to 2.0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |