EN 1.5024 Steel vs. Solder Alloy 704
EN 1.5024 steel belongs to the iron alloys classification, while solder alloy 704 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5024 steel and the bottom bar is solder alloy 704.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 470 | |
| 14 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 51 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 72 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1930 | |
| 55 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 62 |
| Melting Completion (Liquidus), °C | 1440 | |
| 240 |
| Melting Onset (Solidus), °C | 1400 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 220 |
| Thermal Conductivity, W/m-K | 50 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 19 |
| Embodied Energy, MJ/kg | 19 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 17 |
| Strength to Weight: Axial, points | 24 to 69 | |
| 2.1 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 4.3 |
| Thermal Diffusivity, mm2/s | 14 | |
| 30 |
| Thermal Shock Resistance, points | 20 to 58 | |
| 3.5 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0.42 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 96.7 to 97.6 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 1.5 to 2.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 4.8 to 5.2 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Tin (Sn), % | 0 | |
| 94.3 to 95.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |