EN 1.5024 Steel vs. C10500 Copper

EN 1.5024 steel belongs to the iron alloys classification, while C10500 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.5024 steel and the bottom bar is C10500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 72
43
Tensile Strength: Ultimate (UTS), MPa 670 to 1930
220 to 400

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Maximum Temperature: Mechanical, °C 400
200
Melting Completion (Liquidus), °C 1440
1080
Melting Onset (Solidus), °C 1400
1080
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 50
390
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
100
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
100

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
32
Density, g/cm3 7.7
9.0
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 19
42
Embodied Water, L/kg 45
350

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 24 to 69
6.8 to 12
Strength to Weight: Bending, points 22 to 45
9.1 to 14
Thermal Diffusivity, mm2/s 14
110
Thermal Shock Resistance, points 20 to 58
7.8 to 14

Alloy Composition

Carbon (C), % 0.42 to 0.5
0
Copper (Cu), % 0
99.89 to 99.966
Iron (Fe), % 96.7 to 97.6
0
Manganese (Mn), % 0.5 to 0.8
0
Oxygen (O), % 0
0 to 0.0010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 1.5 to 2.0
0
Silver (Ag), % 0
0.034 to 0.060
Sulfur (S), % 0 to 0.025
0
Residuals, % 0
0 to 0.050