MakeItFrom.com
Menu (ESC)

EN 1.5026 Steel vs. Solder Alloy 601

EN 1.5026 steel belongs to the iron alloys classification, while solder alloy 601 belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.5026 steel and the bottom bar is solder alloy 601.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
5.0
Elastic (Young's, Tensile) Modulus, GPa 190
31
Poisson's Ratio 0.29
0.41
Shear Modulus, GPa 72
11
Tensile Strength: Ultimate (UTS), MPa 660 to 1980
12

Thermal Properties

Latent Heat of Fusion, J/g 280
43
Melting Completion (Liquidus), °C 1440
120
Melting Onset (Solidus), °C 1390
120
Specific Heat Capacity, J/kg-K 480
230
Thermal Conductivity, W/m-K 47
34
Thermal Expansion, µm/m-K 13
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
14

Otherwise Unclassified Properties

Density, g/cm3 7.7
7.3
Embodied Water, L/kg 46
1330

Common Calculations

Stiffness to Weight: Axial, points 13
2.3
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 24 to 71
0.45
Strength to Weight: Bending, points 22 to 45
1.6
Thermal Diffusivity, mm2/s 13
20
Thermal Shock Resistance, points 20 to 60
1.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.52 to 0.6
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
51 to 52.5
Iron (Fe), % 96.5 to 97.3
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0.6 to 0.9
0
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 1.6 to 2.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
47.5 to 48.5
Zinc (Zn), % 0
0 to 0.0010