EN 1.5026 Steel vs. C85900 Brass
EN 1.5026 steel belongs to the iron alloys classification, while C85900 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5026 steel and the bottom bar is C85900 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 480 | |
| 85 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1980 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 130 |
| Melting Completion (Liquidus), °C | 1440 | |
| 830 |
| Melting Onset (Solidus), °C | 1390 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 47 | |
| 89 |
| Thermal Expansion, µm/m-K | 13 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 24 |
| Density, g/cm3 | 7.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.9 |
| Embodied Energy, MJ/kg | 19 | |
| 49 |
| Embodied Water, L/kg | 46 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 24 to 71 | |
| 16 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 17 |
| Thermal Diffusivity, mm2/s | 13 | |
| 29 |
| Thermal Shock Resistance, points | 20 to 60 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.1 to 0.6 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Boron (B), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 | |
| 58 to 62 |
| Iron (Fe), % | 96.5 to 97.3 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.010 |
| Silicon (Si), % | 1.6 to 2.0 | |
| 0 to 0.25 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.1 to 0.65 |
| Tin (Sn), % | 0 | |
| 0 to 1.5 |
| Zinc (Zn), % | 0 | |
| 31 to 41 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.7 |