EN 1.5113 Steel vs. 712.0 Aluminum
EN 1.5113 steel belongs to the iron alloys classification, while 712.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.5113 steel and the bottom bar is 712.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 270 | |
| 75 to 90 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 70 |
| Elongation at Break, % | 11 to 18 | |
| 4.5 to 4.7 |
| Fatigue Strength, MPa | 220 to 470 | |
| 140 to 180 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 72 | |
| 27 |
| Shear Strength, MPa | 360 to 540 | |
| 180 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 900 | |
| 250 to 260 |
| Tensile Strength: Yield (Proof), MPa | 320 to 770 | |
| 180 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 190 |
| Melting Completion (Liquidus), °C | 1450 | |
| 640 |
| Melting Onset (Solidus), °C | 1410 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 870 |
| Thermal Conductivity, W/m-K | 52 | |
| 160 |
| Thermal Expansion, µm/m-K | 13 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.0 |
| Embodied Energy, MJ/kg | 19 | |
| 150 |
| Embodied Water, L/kg | 48 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 96 | |
| 11 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 1570 | |
| 240 to 270 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 46 |
| Strength to Weight: Axial, points | 21 to 32 | |
| 24 to 25 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 30 to 31 |
| Thermal Diffusivity, mm2/s | 14 | |
| 62 |
| Thermal Shock Resistance, points | 17 to 26 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 90.7 to 94 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.4 to 0.6 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 97 to 97.5 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 0.5 to 0.65 |
| Manganese (Mn), % | 1.6 to 1.8 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.9 to 1.1 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.25 |
| Zinc (Zn), % | 0 | |
| 5.0 to 6.5 |
| Residuals, % | 0 | |
| 0 to 0.2 |