EN 1.5113 Steel vs. EN 1.1151 Steel
Both EN 1.5113 steel and EN 1.1151 steel are iron alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.5113 steel and the bottom bar is EN 1.1151 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 to 270 | |
130 to 150 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 11 to 18 | |
21 to 26 |
Fatigue Strength, MPa | 220 to 470 | |
180 to 240 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 72 | |
73 |
Shear Strength, MPa | 360 to 540 | |
300 to 330 |
Tensile Strength: Ultimate (UTS), MPa | 580 to 900 | |
460 to 520 |
Tensile Strength: Yield (Proof), MPa | 320 to 770 | |
240 to 340 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
400 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 52 | |
50 |
Thermal Expansion, µm/m-K | 13 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.0 | |
2.1 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.4 |
Embodied Energy, MJ/kg | 19 | |
19 |
Embodied Water, L/kg | 48 | |
47 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 96 | |
98 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 1570 | |
160 to 310 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 21 to 32 | |
16 to 18 |
Strength to Weight: Bending, points | 20 to 27 | |
17 to 18 |
Thermal Diffusivity, mm2/s | 14 | |
13 |
Thermal Shock Resistance, points | 17 to 26 | |
15 to 16 |
Alloy Composition
Carbon (C), % | 0 to 0.1 | |
0.17 to 0.24 |
Chromium (Cr), % | 0 | |
0 to 0.4 |
Iron (Fe), % | 97 to 97.5 | |
97.7 to 99.43 |
Manganese (Mn), % | 1.6 to 1.8 | |
0.4 to 0.7 |
Molybdenum (Mo), % | 0 | |
0 to 0.1 |
Nickel (Ni), % | 0 | |
0 to 0.4 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.035 |
Silicon (Si), % | 0.9 to 1.1 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.035 |