EN 1.5113 Steel vs. SAE-AISI 1330 Steel
Both EN 1.5113 steel and SAE-AISI 1330 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.5113 steel and the bottom bar is SAE-AISI 1330 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 to 270 | |
150 to 210 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 11 to 18 | |
11 to 23 |
Fatigue Strength, MPa | 220 to 470 | |
210 to 380 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 72 | |
73 |
Shear Strength, MPa | 360 to 540 | |
330 to 430 |
Tensile Strength: Ultimate (UTS), MPa | 580 to 900 | |
520 to 710 |
Tensile Strength: Yield (Proof), MPa | 320 to 770 | |
290 to 610 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
400 |
Melting Completion (Liquidus), °C | 1450 | |
1460 |
Melting Onset (Solidus), °C | 1410 | |
1410 |
Specific Heat Capacity, J/kg-K | 480 | |
470 |
Thermal Conductivity, W/m-K | 52 | |
51 |
Thermal Expansion, µm/m-K | 13 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
8.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.0 | |
1.9 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.4 |
Embodied Energy, MJ/kg | 19 | |
19 |
Embodied Water, L/kg | 48 | |
48 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 96 | |
76 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 1570 | |
230 to 990 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 21 to 32 | |
19 to 25 |
Strength to Weight: Bending, points | 20 to 27 | |
18 to 23 |
Thermal Diffusivity, mm2/s | 14 | |
14 |
Thermal Shock Resistance, points | 17 to 26 | |
17 to 23 |
Alloy Composition
Carbon (C), % | 0 to 0.1 | |
0.28 to 0.33 |
Iron (Fe), % | 97 to 97.5 | |
97.3 to 98 |
Manganese (Mn), % | 1.6 to 1.8 | |
1.6 to 1.9 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.035 |
Silicon (Si), % | 0.9 to 1.1 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.040 |