EN 1.5408 Steel vs. SAE-AISI 8645 Steel

Both EN 1.5408 steel and SAE-AISI 8645 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.5408 steel and the bottom bar is SAE-AISI 8645 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 160
180 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 460 to 1620
600 to 670

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 48
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 57
21 to 24
Strength to Weight: Bending, points 17 to 39
20 to 22
Thermal Diffusivity, mm2/s 13
10
Thermal Shock Resistance, points 13 to 48
18 to 20

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.28 to 0.32
0.43 to 0.48
Chromium (Cr), % 0 to 0.3
0.4 to 0.6
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.7 to 98.8
96.5 to 97.7
Manganese (Mn), % 0.8 to 1.0
0.75 to 1.0
Molybdenum (Mo), % 0.080 to 0.12
0.15 to 0.25
Nickel (Ni), % 0
0.4 to 0.7
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.3
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040