EN 1.5408 Steel vs. N07773 Nickel
EN 1.5408 steel belongs to the iron alloys classification, while N07773 nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.5408 steel and the bottom bar is N07773 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 64 to 69 | |
| 56 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1620 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 990 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1510 |
| Melting Onset (Solidus), °C | 1420 | |
| 1460 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 13 |
| Embodied Energy, MJ/kg | 19 | |
| 180 |
| Embodied Water, L/kg | 48 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 57 | |
| 23 |
| Strength to Weight: Bending, points | 17 to 39 | |
| 21 |
| Thermal Shock Resistance, points | 13 to 48 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 2.0 |
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.28 to 0.32 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.3 | |
| 18 to 27 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 97.7 to 98.8 | |
| 0 to 32 |
| Manganese (Mn), % | 0.8 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.080 to 0.12 | |
| 2.5 to 5.5 |
| Nickel (Ni), % | 0 | |
| 45 to 60 |
| Niobium (Nb), % | 0 | |
| 2.5 to 6.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 2.0 |
| Tungsten (W), % | 0 | |
| 0 to 6.0 |