EN 1.5408 Steel vs. S31655 Stainless Steel
Both EN 1.5408 steel and S31655 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.5408 steel and the bottom bar is S31655 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 160 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1620 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 48 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 17 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.3 |
| Embodied Energy, MJ/kg | 19 | |
| 46 |
| Embodied Water, L/kg | 48 | |
| 160 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 57 | |
| 25 |
| Strength to Weight: Bending, points | 17 to 39 | |
| 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 4.0 |
| Thermal Shock Resistance, points | 13 to 48 | |
| 16 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.28 to 0.32 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.3 | |
| 19.5 to 21.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 1.0 |
| Iron (Fe), % | 97.7 to 98.8 | |
| 63.2 to 71.9 |
| Manganese (Mn), % | 0.8 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.080 to 0.12 | |
| 0.5 to 1.5 |
| Nickel (Ni), % | 0 | |
| 8.0 to 9.5 |
| Nitrogen (N), % | 0 | |
| 0.14 to 0.25 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |