EN 1.5414 Steel vs. SAE-AISI 1064 Steel
Both EN 1.5414 steel and SAE-AISI 1064 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.5414 steel and the bottom bar is SAE-AISI 1064 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 180 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 12 to 13 |
| Fatigue Strength, MPa | 250 to 270 | |
| 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 350 to 370 | |
| 430 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 580 | |
| 720 to 730 |
| Tensile Strength: Yield (Proof), MPa | 350 to 380 | |
| 470 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 21 | |
| 19 |
| Embodied Water, L/kg | 50 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 79 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 370 | |
| 600 to 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 25 to 26 |
| Strength to Weight: Bending, points | 19 to 20 | |
| 23 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.2 | |
| 0.6 to 0.7 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 96.4 to 98.7 | |
| 98.4 to 98.9 |
| Manganese (Mn), % | 0.9 to 1.5 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0.45 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.050 |