EN 1.5414 Steel vs. Z41121 Zinc
EN 1.5414 steel belongs to the iron alloys classification, while Z41121 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5414 steel and the bottom bar is Z41121 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 87 |
| Elongation at Break, % | 22 | |
| 50 |
| Poisson's Ratio | 0.29 | |
| 0.25 |
| Shear Modulus, GPa | 73 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 580 | |
| 140 |
| Tensile Strength: Yield (Proof), MPa | 350 to 380 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 90 |
| Melting Completion (Liquidus), °C | 1470 | |
| 410 |
| Melting Onset (Solidus), °C | 1420 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 44 | |
| 110 |
| Thermal Expansion, µm/m-K | 13 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 21 | |
| 54 |
| Embodied Water, L/kg | 50 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 68 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 370 | |
| 79 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 19 to 20 | |
| 6.1 |
| Strength to Weight: Bending, points | 19 to 20 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 12 | |
| 44 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0.080 to 0.49 |
| Iron (Fe), % | 96.4 to 98.7 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.9 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0.45 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 | |
| 0.050 to 0.18 |
| Zinc (Zn), % | 0 | |
| 99.292 to 99.87 |