EN 1.5422 Steel vs. EN 1.8833 Steel

Both EN 1.5422 steel and EN 1.8833 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.5422 steel and the bottom bar is EN 1.8833 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 26
25
Fatigue Strength, MPa 200
280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 520
530
Tensile Strength: Yield (Proof), MPa 270
390

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.7
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 22
21
Embodied Water, L/kg 50
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 200
400
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 10
13
Thermal Shock Resistance, points 15
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.030
Carbon (C), % 0.15 to 0.2
0 to 0.14
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.3 to 98.6
96.8 to 99.98
Manganese (Mn), % 0.8 to 1.2
0 to 1.6
Molybdenum (Mo), % 0.45 to 0.65
0 to 0.2
Nickel (Ni), % 0 to 0.4
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 0.6
0 to 0.5
Sulfur (S), % 0 to 0.020
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0 to 0.050
0 to 0.1