EN 1.5502 Steel vs. AISI 301 Stainless Steel
Both EN 1.5502 steel and AISI 301 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5502 steel and the bottom bar is AISI 301 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 to 160 | |
| 190 to 440 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 20 | |
| 7.4 to 46 |
| Fatigue Strength, MPa | 190 to 290 | |
| 210 to 600 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 280 to 330 | |
| 410 to 860 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 1380 | |
| 590 to 1460 |
| Tensile Strength: Yield (Proof), MPa | 270 to 440 | |
| 230 to 1080 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 840 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1420 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 39 |
| Embodied Water, L/kg | 47 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 210 | |
| 99 to 300 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 520 | |
| 130 to 2970 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 14 to 49 | |
| 21 to 52 |
| Strength to Weight: Bending, points | 15 to 35 | |
| 20 to 37 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.2 |
| Thermal Shock Resistance, points | 12 to 40 | |
| 12 to 31 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.15 to 0.2 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 to 0.3 | |
| 16 to 18 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98 to 99.249 | |
| 70.7 to 78 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 6.0 to 8.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |