EN 1.5502 Steel vs. N08810 Stainless Steel
Both EN 1.5502 steel and N08810 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5502 steel and the bottom bar is N08810 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 20 | |
| 33 |
| Fatigue Strength, MPa | 190 to 290 | |
| 160 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 280 to 330 | |
| 340 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 1380 | |
| 520 |
| Tensile Strength: Yield (Proof), MPa | 270 to 440 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1400 |
| Melting Onset (Solidus), °C | 1420 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 1.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 30 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 5.3 |
| Embodied Energy, MJ/kg | 19 | |
| 76 |
| Embodied Water, L/kg | 47 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 210 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 520 | |
| 100 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 49 | |
| 18 |
| Strength to Weight: Bending, points | 15 to 35 | |
| 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 12 to 40 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.15 to 0.6 |
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.15 to 0.2 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 0 to 0.3 | |
| 19 to 23 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.75 |
| Iron (Fe), % | 98 to 99.249 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |