EN 1.5503 Steel vs. 2024 Aluminum
EN 1.5503 steel belongs to the iron alloys classification, while 2024 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.5503 steel and the bottom bar is 2024 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 71 |
| Elongation at Break, % | 12 to 17 | |
| 4.0 to 16 |
| Fatigue Strength, MPa | 180 to 280 | |
| 90 to 180 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 27 |
| Shear Strength, MPa | 270 to 320 | |
| 130 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 520 | |
| 200 to 540 |
| Tensile Strength: Yield (Proof), MPa | 270 to 430 | |
| 100 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 640 |
| Melting Onset (Solidus), °C | 1420 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 880 |
| Thermal Conductivity, W/m-K | 52 | |
| 120 |
| Thermal Expansion, µm/m-K | 13 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 90 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.3 |
| Embodied Energy, MJ/kg | 18 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 81 | |
| 20 to 68 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 490 | |
| 70 to 1680 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 46 |
| Strength to Weight: Axial, points | 14 to 19 | |
| 18 to 50 |
| Strength to Weight: Bending, points | 15 to 18 | |
| 25 to 49 |
| Thermal Diffusivity, mm2/s | 14 | |
| 46 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 8.6 to 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 90.7 to 94.7 |
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.16 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.25 | |
| 3.8 to 4.9 |
| Iron (Fe), % | 98.4 to 99.239 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 1.2 to 1.8 |
| Manganese (Mn), % | 0.6 to 0.8 | |
| 0.3 to 0.9 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |