EN 1.5503 Steel vs. C22600 Bronze
EN 1.5503 steel belongs to the iron alloys classification, while C22600 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.5503 steel and the bottom bar is C22600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 12 to 17 | |
| 2.5 to 33 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 42 |
| Shear Strength, MPa | 270 to 320 | |
| 220 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 520 | |
| 330 to 570 |
| Tensile Strength: Yield (Proof), MPa | 270 to 430 | |
| 270 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1420 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 52 | |
| 170 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 28 |
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 18 | |
| 42 |
| Embodied Water, L/kg | 46 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 81 | |
| 14 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 490 | |
| 330 to 1070 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 14 to 19 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 15 to 18 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 52 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 11 to 19 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.16 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 86 to 89 |
| Iron (Fe), % | 98.4 to 99.239 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.6 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 10.7 to 14 |
| Residuals, % | 0 | |
| 0 to 0.2 |