EN 1.5508 Steel vs. EN 1.8823 Steel
Both EN 1.5508 steel and EN 1.8823 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.5508 steel and the bottom bar is EN 1.8823 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 130 to 180 | |
160 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 11 to 20 | |
25 |
Fatigue Strength, MPa | 210 to 320 | |
270 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Shear Strength, MPa | 300 to 360 | |
340 |
Tensile Strength: Ultimate (UTS), MPa | 420 to 1460 | |
530 |
Tensile Strength: Yield (Proof), MPa | 310 to 490 | |
360 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
410 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 51 | |
47 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
7.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
8.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.9 | |
2.4 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.6 |
Embodied Energy, MJ/kg | 19 | |
22 |
Embodied Water, L/kg | 47 | |
49 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 230 | |
120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 640 | |
360 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 15 to 52 | |
19 |
Strength to Weight: Bending, points | 16 to 36 | |
19 |
Thermal Diffusivity, mm2/s | 14 | |
13 |
Thermal Shock Resistance, points | 12 to 43 | |
16 |
Alloy Composition
Aluminum (Al), % | 0 | |
0.015 to 0.034 |
Boron (B), % | 0.00080 to 0.0050 | |
0 |
Carbon (C), % | 0.2 to 0.25 | |
0 to 0.16 |
Chromium (Cr), % | 0 to 0.3 | |
0 to 0.35 |
Copper (Cu), % | 0 to 0.25 | |
0 to 0.6 |
Iron (Fe), % | 97.9 to 99.199 | |
95.6 to 99.985 |
Manganese (Mn), % | 0.6 to 0.9 | |
0 to 1.7 |
Molybdenum (Mo), % | 0 | |
0 to 0.13 |
Nickel (Ni), % | 0 | |
0 to 0.55 |
Niobium (Nb), % | 0 | |
0 to 0.060 |
Nitrogen (N), % | 0 | |
0 to 0.017 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.035 |
Silicon (Si), % | 0 to 0.3 | |
0 to 0.55 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.030 |
Titanium (Ti), % | 0 | |
0 to 0.060 |
Vanadium (V), % | 0 | |
0 to 0.12 |