EN 1.5511 Steel vs. AISI 304N Stainless Steel

Both EN 1.5511 steel and AISI 304N stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.5511 steel and the bottom bar is AISI 304N stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 170
190 to 360
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Tensile Strength: Ultimate (UTS), MPa 490 to 580
620 to 1180

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 46
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 20
22 to 42
Strength to Weight: Bending, points 18 to 20
21 to 32
Thermal Diffusivity, mm2/s 14
4.2
Thermal Shock Resistance, points 15 to 17
14 to 26

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.32 to 0.39
0 to 0.080
Chromium (Cr), % 0
18 to 20
Iron (Fe), % 98.3 to 99.159
66.4 to 73.9
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Nickel (Ni), % 0
8.0 to 10.5
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030