EN 1.5511 Steel vs. AWS ERTi-7

EN 1.5511 steel belongs to the iron alloys classification, while AWS ERTi-7 belongs to the titanium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.5511 steel and the bottom bar is AWS ERTi-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
40
Tensile Strength: Ultimate (UTS), MPa 490 to 580
340

Thermal Properties

Latent Heat of Fusion, J/g 250
420
Maximum Temperature: Mechanical, °C 400
320
Melting Completion (Liquidus), °C 1460
1670
Melting Onset (Solidus), °C 1420
1620
Specific Heat Capacity, J/kg-K 470
540
Thermal Conductivity, W/m-K 51
21
Thermal Expansion, µm/m-K 13
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
7.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
4.5
Embodied Carbon, kg CO2/kg material 1.4
47
Embodied Energy, MJ/kg 19
800
Embodied Water, L/kg 46
470

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
35
Strength to Weight: Axial, points 17 to 20
21
Strength to Weight: Bending, points 18 to 20
24
Thermal Diffusivity, mm2/s 14
8.8
Thermal Shock Resistance, points 15 to 17
26

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.32 to 0.39
0 to 0.030
Hydrogen (H), % 0
0 to 0.0080
Iron (Fe), % 98.3 to 99.159
0 to 0.12
Manganese (Mn), % 0.5 to 0.8
0
Nitrogen (N), % 0
0 to 0.015
Oxygen (O), % 0
0.080 to 0.16
Palladium (Pd), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
99.417 to 99.8