EN 1.5511 Steel vs. EN 1.4518 Stainless Steel

Both EN 1.5511 steel and EN 1.4518 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.5511 steel and the bottom bar is EN 1.4518 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
79
Tensile Strength: Ultimate (UTS), MPa 490 to 580
490

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
4.0
Embodied Energy, MJ/kg 19
55
Embodied Water, L/kg 46
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17 to 20
17
Strength to Weight: Bending, points 18 to 20
18
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 15 to 17
14

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0
18 to 20
Iron (Fe), % 98.3 to 99.159
61.4 to 70
Manganese (Mn), % 0.5 to 0.8
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0
9.0 to 12
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030