EN 1.5511 Steel vs. Solder Alloy 162
EN 1.5511 steel belongs to the iron alloys classification, while solder alloy 162 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.5511 steel and the bottom bar is solder alloy 162.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
35 |
Poisson's Ratio | 0.29 | |
0.4 |
Shear Modulus, GPa | 72 | |
12 |
Tensile Strength: Ultimate (UTS), MPa | 490 to 580 | |
41 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
44 |
Melting Completion (Liquidus), °C | 1460 | |
220 |
Melting Onset (Solidus), °C | 1420 | |
180 |
Specific Heat Capacity, J/kg-K | 470 | |
180 |
Thermal Conductivity, W/m-K | 51 | |
47 |
Thermal Expansion, µm/m-K | 13 | |
25 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
11 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
10 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
9.3 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
9.4 |
Embodied Energy, MJ/kg | 19 | |
160 |
Embodied Water, L/kg | 46 | |
830 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
2.1 |
Stiffness to Weight: Bending, points | 24 | |
12 |
Strength to Weight: Axial, points | 17 to 20 | |
1.2 |
Strength to Weight: Bending, points | 18 to 20 | |
2.8 |
Thermal Diffusivity, mm2/s | 14 | |
28 |
Thermal Shock Resistance, points | 15 to 17 | |
3.3 |
Alloy Composition
Aluminum (Al), % | 0.020 to 0.060 | |
0 to 0.0010 |
Antimony (Sb), % | 0 | |
0 to 0.2 |
Arsenic (As), % | 0 | |
0 to 0.030 |
Bismuth (Bi), % | 0 | |
0 to 0.1 |
Boron (B), % | 0.00080 to 0.0050 | |
0 |
Cadmium (Cd), % | 0 | |
0 to 0.0020 |
Carbon (C), % | 0.32 to 0.39 | |
0 |
Copper (Cu), % | 0 | |
1.2 to 1.6 |
Gold (Au), % | 0 | |
0 to 0.050 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 98.3 to 99.159 | |
0 to 0.020 |
Lead (Pb), % | 0 | |
47.3 to 49.3 |
Manganese (Mn), % | 0.5 to 0.8 | |
0 |
Nickel (Ni), % | 0 | |
0 to 0.010 |
Phosphorus (P), % | 0 to 0.030 | |
0 |
Silicon (Si), % | 0 to 0.4 | |
0 |
Silver (Ag), % | 0 | |
0 to 0.1 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Tin (Sn), % | 0 | |
49.5 to 50.5 |
Zinc (Zn), % | 0 | |
0 to 0.0010 |