EN 1.5514 Steel vs. ASTM A302 Alloy Steel
Both EN 1.5514 steel and ASTM A302 alloy steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.5514 steel and the bottom bar is ASTM A302 alloy steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 170 | |
| 180 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 1680 | |
| 590 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 49 | |
| 39 to 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.2 to 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.2 to 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 2.4 to 3.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 to 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 to 1.6 |
| Embodied Energy, MJ/kg | 19 | |
| 20 to 21 |
| Embodied Water, L/kg | 47 | |
| 48 to 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 60 | |
| 21 to 22 |
| Strength to Weight: Bending, points | 17 to 40 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 13 | |
| 10 to 14 |
| Thermal Shock Resistance, points | 14 to 50 | |
| 17 to 18 |