EN 1.5514 Steel vs. Nickel 30

EN 1.5514 steel belongs to the iron alloys classification, while nickel 30 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.5514 steel and the bottom bar is nickel 30.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 470 to 1680
660

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1020
Melting Completion (Liquidus), °C 1460
1480
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 49
10
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
60
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.4
9.4
Embodied Energy, MJ/kg 19
130
Embodied Water, L/kg 47
290

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17 to 60
22
Strength to Weight: Bending, points 17 to 40
20
Thermal Diffusivity, mm2/s 13
2.7
Thermal Shock Resistance, points 14 to 50
18

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.3 to 0.35
0 to 0.030
Chromium (Cr), % 0 to 0.3
28 to 31.5
Cobalt (Co), % 0
0 to 5.0
Copper (Cu), % 0 to 0.25
1.0 to 2.4
Iron (Fe), % 97.8 to 99.099
13 to 17
Manganese (Mn), % 0.6 to 0.9
0 to 0.030
Molybdenum (Mo), % 0
4.0 to 6.0
Nickel (Ni), % 0
30.2 to 52.2
Niobium (Nb), % 0
0.3 to 1.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 0.8
Sulfur (S), % 0 to 0.025
0 to 0.020
Tungsten (W), % 0
1.5 to 4.0