EN 1.5514 Steel vs. N06650 Nickel

EN 1.5514 steel belongs to the iron alloys classification, while N06650 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.5514 steel and the bottom bar is N06650 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 470 to 1680
900

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1500
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
60
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.4
10
Embodied Energy, MJ/kg 19
140
Embodied Water, L/kg 47
270

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 17 to 60
29
Strength to Weight: Bending, points 17 to 40
24
Thermal Shock Resistance, points 14 to 50
24

Alloy Composition

Aluminum (Al), % 0
0.050 to 0.5
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.3 to 0.35
0 to 0.030
Chromium (Cr), % 0 to 0.3
19 to 21
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 97.8 to 99.099
12 to 16
Manganese (Mn), % 0.6 to 0.9
0 to 0.5
Molybdenum (Mo), % 0
9.5 to 12.5
Nickel (Ni), % 0
44.4 to 58.9
Niobium (Nb), % 0
0.050 to 0.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Tungsten (W), % 0
0.5 to 2.5