EN 1.5515 Steel vs. SAE-AISI 1547 Steel
Both EN 1.5515 steel and SAE-AISI 1547 steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.5515 steel and the bottom bar is SAE-AISI 1547 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 170 | |
| 200 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 64 to 69 | |
| 32 to 40 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1760 | |
| 740 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 63 | |
| 26 to 28 |
| Strength to Weight: Bending, points | 18 to 41 | |
| 23 to 24 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 52 | |
| 23 to 25 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.35 to 0.4 | |
| 0.43 to 0.51 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 97.8 to 98.9 | |
| 97.8 to 98.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.050 |