EN 1.5520 Steel vs. AISI 201 Stainless Steel

Both EN 1.5520 steel and AISI 201 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5520 steel and the bottom bar is AISI 201 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120 to 170
200 to 440
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 21
4.6 to 51
Fatigue Strength, MPa 210 to 300
280 to 600
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 290 to 340
450 to 840
Tensile Strength: Ultimate (UTS), MPa 410 to 1410
650 to 1450
Tensile Strength: Yield (Proof), MPa 300 to 480
300 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
880
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 19
38
Embodied Water, L/kg 48
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 42 to 230
61 to 340
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 600
230 to 2970
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15 to 50
23 to 52
Strength to Weight: Bending, points 16 to 36
22 to 37
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 12 to 41
14 to 32

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.15 to 0.2
0 to 0.15
Chromium (Cr), % 0 to 0.3
16 to 18
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.7 to 98.9
67.5 to 75
Manganese (Mn), % 0.9 to 1.2
5.5 to 7.5
Nickel (Ni), % 0
3.5 to 5.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.060
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030