EN 1.5520 Steel vs. EN 1.8201 Steel

Both EN 1.5520 steel and EN 1.8201 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5520 steel and the bottom bar is EN 1.8201 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120 to 170
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 21
20
Fatigue Strength, MPa 210 to 300
310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 290 to 340
390
Tensile Strength: Ultimate (UTS), MPa 410 to 1410
630
Tensile Strength: Yield (Proof), MPa 300 to 480
450

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
450
Melting Completion (Liquidus), °C 1460
1500
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
7.0
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
2.5
Embodied Energy, MJ/kg 19
36
Embodied Water, L/kg 48
59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 42 to 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 600
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 50
22
Strength to Weight: Bending, points 16 to 36
20
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 12 to 41
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Boron (B), % 0.00080 to 0.0050
0.0010 to 0.0060
Carbon (C), % 0.15 to 0.2
0.040 to 0.1
Chromium (Cr), % 0 to 0.3
1.9 to 2.6
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.7 to 98.9
93.6 to 96.2
Manganese (Mn), % 0.9 to 1.2
0.1 to 0.6
Molybdenum (Mo), % 0
0.050 to 0.3
Niobium (Nb), % 0
0.020 to 0.080
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0.0050 to 0.060
Tungsten (W), % 0
1.5 to 1.8
Vanadium (V), % 0
0.2 to 0.3