EN 1.5521 Steel vs. SAE-AISI 1141 Steel
Both EN 1.5521 steel and SAE-AISI 1141 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.5521 steel and the bottom bar is SAE-AISI 1141 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 180 | |
| 210 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 21 | |
| 11 to 17 |
| Fatigue Strength, MPa | 210 to 310 | |
| 270 to 430 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 59 to 72 | |
| 34 to 39 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 310 to 360 | |
| 460 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 1390 | |
| 740 to 810 |
| Tensile Strength: Yield (Proof), MPa | 300 to 490 | |
| 400 to 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 230 | |
| 86 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 630 | |
| 430 to 1290 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 49 | |
| 26 to 29 |
| Strength to Weight: Bending, points | 16 to 35 | |
| 23 to 25 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 13 to 41 | |
| 24 to 26 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.16 to 0.2 | |
| 0.37 to 0.45 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98 to 98.9 | |
| 97.7 to 98.2 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.080 to 0.13 |