EN 1.5522 Steel vs. ASTM A514 Steel

Both EN 1.5522 steel and ASTM A514 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.5522 steel and the bottom bar is ASTM A514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 190
240 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 21
18 to 21
Fatigue Strength, MPa 210 to 330
470 to 540
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320 to 380
490 to 520
Tensile Strength: Ultimate (UTS), MPa 450 to 1490
790 to 830
Tensile Strength: Yield (Proof), MPa 300 to 520
690 to 770

Thermal Properties

Latent Heat of Fusion, J/g 250
250 to 260
Maximum Temperature: Mechanical, °C 400
400 to 440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
37 to 51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2 to 7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.3 to 8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.3 to 3.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 1.4
1.6 to 1.8
Embodied Energy, MJ/kg 19
21 to 25
Embodied Water, L/kg 47
48 to 57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 45 to 250
140 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 720
1280 to 1590
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 53
28 to 29
Strength to Weight: Bending, points 17 to 37
24 to 25
Thermal Diffusivity, mm2/s 14
10 to 14
Thermal Shock Resistance, points 13 to 44
23 to 24