EN 1.5522 Steel vs. SAE-AISI 12L14 Steel
Both EN 1.5522 steel and SAE-AISI 12L14 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.5522 steel and the bottom bar is SAE-AISI 12L14 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 190 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 21 | |
| 11 to 25 |
| Fatigue Strength, MPa | 210 to 330 | |
| 190 to 290 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 59 to 69 | |
| 39 to 51 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 320 to 380 | |
| 280 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 1490 | |
| 440 to 620 |
| Tensile Strength: Yield (Proof), MPa | 300 to 520 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 18 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 250 | |
| 64 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 720 | |
| 180 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 53 | |
| 15 to 22 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 13 to 44 | |
| 14 to 20 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.2 to 0.24 | |
| 0 to 0.15 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98 to 98.9 | |
| 97.9 to 98.7 |
| Lead (Pb), % | 0 | |
| 0.15 to 0.35 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0.85 to 1.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0.040 to 0.090 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.26 to 0.35 |