EN 1.5522 Steel vs. C40500 Penny Bronze
EN 1.5522 steel belongs to the iron alloys classification, while C40500 penny bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.5522 steel and the bottom bar is C40500 penny bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 11 to 21 | |
| 3.0 to 49 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Shear Strength, MPa | 320 to 380 | |
| 210 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 1490 | |
| 270 to 540 |
| Tensile Strength: Yield (Proof), MPa | 300 to 520 | |
| 79 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 190 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1060 |
| Melting Onset (Solidus), °C | 1420 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 51 | |
| 160 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 30 |
| Density, g/cm3 | 7.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 43 |
| Embodied Water, L/kg | 47 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 250 | |
| 16 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 720 | |
| 28 to 1200 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 53 | |
| 8.5 to 17 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 10 to 17 |
| Thermal Diffusivity, mm2/s | 14 | |
| 48 |
| Thermal Shock Resistance, points | 13 to 44 | |
| 9.5 to 19 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.2 to 0.24 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 94 to 96 |
| Iron (Fe), % | 98 to 98.9 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Zinc (Zn), % | 0 | |
| 2.1 to 5.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |