EN 1.5522 Steel vs. C61000 Bronze
EN 1.5522 steel belongs to the iron alloys classification, while C61000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.5522 steel and the bottom bar is C61000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 11 to 21 | |
| 29 to 50 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 42 |
| Shear Strength, MPa | 320 to 380 | |
| 280 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 1490 | |
| 390 to 460 |
| Tensile Strength: Yield (Proof), MPa | 300 to 520 | |
| 150 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 210 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1420 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Conductivity, W/m-K | 51 | |
| 69 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 29 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 19 | |
| 49 |
| Embodied Water, L/kg | 47 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 250 | |
| 110 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 720 | |
| 100 to 160 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 53 | |
| 13 to 15 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 14 to 16 |
| Thermal Diffusivity, mm2/s | 14 | |
| 19 |
| Thermal Shock Resistance, points | 13 to 44 | |
| 14 to 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.0 to 8.5 |
| Boron (B), % | 0.00080 to 0.0050 | |
| 0 |
| Carbon (C), % | 0.2 to 0.24 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 90.2 to 94 |
| Iron (Fe), % | 98 to 98.9 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |