EN 1.5525 Steel vs. EN 1.4595 Stainless Steel

Both EN 1.5525 steel and EN 1.4595 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.5525 steel and the bottom bar is EN 1.4595 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 21
29
Fatigue Strength, MPa 210 to 310
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 310 to 350
310
Tensile Strength: Ultimate (UTS), MPa 440 to 1440
470
Tensile Strength: Yield (Proof), MPa 300 to 490
250

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
810
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
30
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
10
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 19
34
Embodied Water, L/kg 48
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 240
110
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 640
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 51
17
Strength to Weight: Bending, points 16 to 36
17
Thermal Diffusivity, mm2/s 13
8.1
Thermal Shock Resistance, points 13 to 42
17

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.18 to 0.23
0 to 0.020
Chromium (Cr), % 0 to 0.3
14 to 16
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 97.7 to 98.9
81.3 to 85.8
Manganese (Mn), % 0.9 to 1.2
0 to 1.0
Niobium (Nb), % 0
0.2 to 0.6
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015