EN 1.5525 Steel vs. EN 1.5520 Steel
Both EN 1.5525 steel and EN 1.5520 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.5525 steel and the bottom bar is EN 1.5520 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 180 | |
| 120 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 21 | |
| 11 to 21 |
| Fatigue Strength, MPa | 210 to 310 | |
| 210 to 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 62 to 73 | |
| 62 to 75 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 310 to 350 | |
| 290 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 1440 | |
| 410 to 1410 |
| Tensile Strength: Yield (Proof), MPa | 300 to 490 | |
| 300 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 48 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 240 | |
| 42 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 640 | |
| 240 to 600 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 51 | |
| 15 to 50 |
| Strength to Weight: Bending, points | 16 to 36 | |
| 16 to 36 |
| Thermal Diffusivity, mm2/s | 13 | |
| 13 |
| Thermal Shock Resistance, points | 13 to 42 | |
| 12 to 41 |
Alloy Composition
| Boron (B), % | 0.00080 to 0.0050 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.18 to 0.23 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 97.7 to 98.9 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0.9 to 1.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |