EN 1.5525 Steel vs. N08810 Stainless Steel

Both EN 1.5525 steel and N08810 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.5525 steel and the bottom bar is N08810 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 21
33
Fatigue Strength, MPa 210 to 310
160
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 310 to 350
340
Tensile Strength: Ultimate (UTS), MPa 440 to 1440
520
Tensile Strength: Yield (Proof), MPa 300 to 490
200

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.3
Embodied Energy, MJ/kg 19
76
Embodied Water, L/kg 48
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44 to 240
140
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 640
100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 51
18
Strength to Weight: Bending, points 16 to 36
18
Thermal Diffusivity, mm2/s 13
3.0
Thermal Shock Resistance, points 13 to 42
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.18 to 0.23
0.050 to 0.1
Chromium (Cr), % 0 to 0.3
19 to 23
Copper (Cu), % 0 to 0.25
0 to 0.75
Iron (Fe), % 97.7 to 98.9
39.5 to 50.7
Manganese (Mn), % 0.9 to 1.2
0 to 1.5
Nickel (Ni), % 0
30 to 35
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6