EN 1.5526 Steel vs. EN 1.0044 Steel

Both EN 1.5526 steel and EN 1.0044 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.5526 steel and the bottom bar is EN 1.0044 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 170
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 490 to 1650
470

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 47
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17 to 59
17
Strength to Weight: Bending, points 18 to 40
17
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 14 to 49
15

Alloy Composition

Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.27 to 0.32
0 to 0.25
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
0 to 0.6
Iron (Fe), % 97.7 to 98.9
97.4 to 100
Manganese (Mn), % 0.8 to 1.1
0 to 1.6
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0
Sulfur (S), % 0 to 0.025
0 to 0.045