EN 1.5535 Steel vs. EN 2.4668 Nickel

EN 1.5535 steel belongs to the iron alloys classification, while EN 2.4668 nickel belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5535 steel and the bottom bar is EN 2.4668 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 22
14
Fatigue Strength, MPa 210 to 320
590
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
75
Shear Strength, MPa 320 to 370
840
Tensile Strength: Ultimate (UTS), MPa 450 to 1490
1390
Tensile Strength: Yield (Proof), MPa 300 to 500
1160

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 50
13
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
75
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.4
13
Embodied Energy, MJ/kg 19
190
Embodied Water, L/kg 48
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 45 to 250
180
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 680
3490
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 16 to 53
46
Strength to Weight: Bending, points 17 to 37
33
Thermal Diffusivity, mm2/s 13
3.5
Thermal Shock Resistance, points 13 to 44
40

Alloy Composition

Aluminum (Al), % 0
0.3 to 0.7
Boron (B), % 0.00080 to 0.0050
0.0020 to 0.0060
Carbon (C), % 0.2 to 0.25
0.020 to 0.080
Chromium (Cr), % 0 to 0.3
17 to 21
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 97.6 to 98.9
11.2 to 24.6
Manganese (Mn), % 0.9 to 1.2
0 to 0.35
Molybdenum (Mo), % 0
2.8 to 3.3
Nickel (Ni), % 0
50 to 55
Niobium (Nb), % 0
4.7 to 5.5
Phosphorus (P), % 0 to 0.025
0 to 0.015
Silicon (Si), % 0 to 0.3
0 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0.6 to 1.2