EN 1.5535 Steel vs. Nickel 601

EN 1.5535 steel belongs to the iron alloys classification, while nickel 601 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.5535 steel and the bottom bar is nickel 601.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 22
10 to 38
Fatigue Strength, MPa 210 to 320
220 to 380
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 320 to 370
440 to 530
Tensile Strength: Ultimate (UTS), MPa 450 to 1490
660 to 890
Tensile Strength: Yield (Proof), MPa 300 to 500
290 to 800

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
11
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
49
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.4
8.0
Embodied Energy, MJ/kg 19
110
Embodied Water, L/kg 48
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 45 to 250
86 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 680
210 to 1630
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 16 to 53
22 to 30
Strength to Weight: Bending, points 17 to 37
20 to 25
Thermal Diffusivity, mm2/s 13
2.8
Thermal Shock Resistance, points 13 to 44
17 to 23

Alloy Composition

Aluminum (Al), % 0
1.0 to 1.7
Boron (B), % 0.00080 to 0.0050
0
Carbon (C), % 0.2 to 0.25
0 to 0.1
Chromium (Cr), % 0 to 0.3
21 to 25
Copper (Cu), % 0 to 0.25
0 to 1.0
Iron (Fe), % 97.6 to 98.9
7.7 to 20
Manganese (Mn), % 0.9 to 1.2
0 to 1.0
Nickel (Ni), % 0
58 to 63
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.3
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.015

Comparable Variants