EN 1.5538 Steel vs. EN 1.5507 Steel
Both EN 1.5538 steel and EN 1.5507 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.5538 steel and the bottom bar is EN 1.5507 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 190 | |
| 140 to 260 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 64 to 69 | |
| 58 to 72 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 530 to 1810 | |
| 450 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 49 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 2.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 48 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 64 | |
| 16 to 31 |
| Strength to Weight: Bending, points | 19 to 42 | |
| 17 to 26 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 16 to 53 | |
| 13 to 26 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.080 |
| Boron (B), % | 0.00080 to 0.0050 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.35 to 0.4 | |
| 0.21 to 0.25 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0.25 to 0.35 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 97.2 to 98.5 | |
| 97.8 to 98.7 |
| Manganese (Mn), % | 1.2 to 1.5 | |
| 0.8 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.060 |