EN 1.5638 Steel vs. SAE-AISI 1213 Steel

Both EN 1.5638 steel and SAE-AISI 1213 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.5638 steel and the bottom bar is SAE-AISI 1213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
140 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
11 to 29
Fatigue Strength, MPa 290
200 to 290
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 580
440 to 600
Tensile Strength: Yield (Proof), MPa 410
260 to 470

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 52
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
63 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 450
180 to 580
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
16 to 21
Strength to Weight: Bending, points 20
17 to 20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
14 to 19

Alloy Composition

Carbon (C), % 0.060 to 0.12
0 to 0.13
Iron (Fe), % 94.4 to 96.4
98.4 to 99
Manganese (Mn), % 0.5 to 0.8
0.7 to 1.0
Nickel (Ni), % 3.0 to 4.0
0
Phosphorus (P), % 0 to 0.020
0.070 to 0.12
Silicon (Si), % 0 to 0.6
0
Sulfur (S), % 0 to 0.015
0.24 to 0.33