EN 1.5662 Steel vs. 1050A Aluminum

EN 1.5662 steel belongs to the iron alloys classification, while 1050A aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.5662 steel and the bottom bar is 1050A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 230
20 to 45
Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 20
1.1 to 33
Fatigue Strength, MPa 380 to 450
22 to 55
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 460 to 470
44 to 97
Tensile Strength: Ultimate (UTS), MPa 740 to 750
68 to 170
Tensile Strength: Yield (Proof), MPa 550 to 660
22 to 150

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 430
170
Melting Completion (Liquidus), °C 1460
660
Melting Onset (Solidus), °C 1410
650
Specific Heat Capacity, J/kg-K 470
900
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.7
59
Electrical Conductivity: Equal Weight (Specific), % IACS 9.8
200

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
9.0
Density, g/cm3 8.0
2.7
Embodied Carbon, kg CO2/kg material 2.3
8.2
Embodied Energy, MJ/kg 31
150
Embodied Water, L/kg 63
1200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 150
1.9 to 19
Resilience: Unit (Modulus of Resilience), kJ/m3 810 to 1150
3.7 to 160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 26
6.9 to 18
Strength to Weight: Bending, points 23
14 to 25
Thermal Shock Resistance, points 22
3.0 to 7.6

Alloy Composition

Aluminum (Al), % 0
99.5 to 100
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
0 to 0.050
Iron (Fe), % 88.6 to 91.2
0 to 0.4
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0.3 to 0.8
0 to 0.050
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 8.5 to 10
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.35
0 to 0.25
Sulfur (S), % 0 to 0.0050
0
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.070