EN 1.5682 Steel vs. EN 1.4303 Stainless Steel

Both EN 1.5682 steel and EN 1.4303 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.5682 steel and the bottom bar is EN 1.4303 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
13 to 49
Fatigue Strength, MPa 400
220 to 320
Impact Strength: V-Notched Charpy, J 68
91 to 98
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 480
420 to 540
Tensile Strength: Ultimate (UTS), MPa 770
590 to 900
Tensile Strength: Yield (Proof), MPa 570
230 to 560

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 430
940
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 9.8
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
17
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.3
3.2
Embodied Energy, MJ/kg 31
46
Embodied Water, L/kg 63
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
110 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 870
140 to 800
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 27
21 to 32
Strength to Weight: Bending, points 23
20 to 26
Thermal Shock Resistance, points 23
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.13
0 to 0.060
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 88.7 to 91.1
64.8 to 72
Manganese (Mn), % 0.3 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 8.5 to 9.5
11 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.0050
0 to 0.015
Vanadium (V), % 0 to 0.050
0